Nanocrystalline cores manufacturer and supplier from TRANSMART: Transmart is a transformer core manufacturer with years of experience, mainly providing nanocrystalline cores, amorphous cores, silicon steel cores, common mode chokes, etc. We specialized in a broad range of tape wound cores in amorphous metal materials, nanocrystalline alloys, silicon electrical steels, and mu metal nickel alloys for a wide variety of applications including solar inverters, home appliance, audio system, etc. Nanocrystalline Ribbons are thin strips of material that have been engineered at the nanoscale to possess unique properties and characteristics. These ribbons are typically made up of highly ordered crystalline structures with grain sizes on the order of a few nanometers, giving them exceptional strength and durability. Read even more details on nanocrystalline transformer core.
Characteristics and application of nanocrystalline magnetic core: High permeability, nanocrystalline Fe73 5Cu1Nb3Si13. 5B9 alloy has high saturation magnetic induction. The material becomes brittle after heat treatment and is easy to be processed into alloy powder. Compared with the nanocrystalline magnetic core wound with strip, the magnetic permeability of the nanocrystalline magnetic core is still very low and the soft magnetic properties are unstable. At present, the urgent problems to be solved are as follows: 1. Effectively control the growth of nanocrystals during heat treatment; 2. Molding of magnetic particle core; 3 Effect of heat treatment specification on soft magnetic properties of magnetic particle core.
Fe based amorphous alloys are competing with silicon steel in power frequency and medium frequency fields. Compared with silicon steel, iron-based amorphous alloy has the following advantages and disadvantages. The saturated magnetic flux density BS of iron-based amorphous alloy is lower than that of silicon steel. The filling coefficient of Fe based amorphous alloy core is 0.84 ~ 0.86. It shows that Fe based amorphous alloy has better resistance to power waveform distortion than silicon steel.
Amorphous Core is preferred choice for transformers required low losses at high frequency. We have amorphous c-cores,amorphous ribbon cores,amorphous cut cores,amorphous core transformers . Please find out more about crgo core material. There are 50% and 80% nickel iron materials available, in which we manufactures Mumetal Toroidal core and Mumetal C-core, for the applications in high quality Current Transformers and power supplies industries.
Hysteresis loss is the iron loss caused by the hysteresis phenomenon in the magnetization process of the iron core. The size of this loss is directly proportional to the area surrounded by the hysteresis loop of the material. The hysteresis loop of silicon steel is narrow, and the hysteresis loss of transformer core made of silicon steel is small, which can greatly reduce its heating degree. Since silicon steel has the above advantages, why not use the whole silicon steel as the iron core and process it into a sheet? rolled silicon steel sheet is selected. It is cut into long pieces according to the size of the required iron core, and then overlapped into “day” shape or “mouth” shape. In principle, in order to reduce eddy current, the thinner the silicon steel sheet, the narrower the spliced strip, and the better the effect. This not only reduces the eddy current loss and temperature rise, but also saves the material of silicon steel sheet. But in fact, when making silicon steel sheet iron core. Not only from the above favorable factors, because making the iron core in that way will greatly increase the working hours and reduce the effective section of the iron core. Therefore, when making transformer iron core with silicon steel sheet, we should start from the specific situation, weigh the advantages and disadvantages and choose the best size. Read more information on https://www.transmartcore.com/.
Commonly used transformer cores are generally made of silicon steel sheets. Silicon steel is a kind of steel with silicon (silicon is also called silicon), and its silicon content is 0.8 ~ 4.8%. The reason why silicon steel is used as the iron core of transformer is that silicon steel itself is a magnetic material with strong magnetic conductivity. In the energized coil, it can produce large magnetic induction intensity, which can reduce the volume of transformer.