Best nanocrystalline cores manufacturer and supplier: One of the key factors to the success of TRANSMART is focusing on basic raw materials research and development. Our ability to tailor the composition and specific heat treatments according to our know-how enables us to design alloys with unique properties for specific customer needs. Transmart is one of the few companies worldwide that have mastered the rapid solidification process where alloys are being produced as a thin strip to its final thickness of typically 16 to 30 um. Toroidal transformers from Transmart toroidal transformer manufacturers offer reliable performance and versatility across a wide range of industries requiring precise power conversion solutions. See additional details at nanocrystalline transformer core.
On the one hand, it can isolate eddy current, and the data is suitable for higher frequencies; On the other hand, due to the gap effect between particles, the data has low permeability and constant permeability; Because the particle size is small, there is basically no skin phenomenon, and the change of permeability with frequency is relatively stable; Moreover, the powder core can be prepared into special-shaped parts of various shapes for different fields; Finally, the damaged strip in industry can be crushed into magnetic powder, and then made into magnetic powder core, which can reduce the loss and improve the use value of data. The magnetoelectric properties of magnetic particle core mainly depend on the permeability of powder material, size and shape of powder, filling coefficient, content of insulating medium, forming pressure and heat treatment process.
Amorphous nanocrystalline alloys are competing with soft ferrite in the field of medium and high frequency. In 10kHz to 50KHz electronic transformer, the working magnetic flux density of iron-based nanocrystalline alloy can reach 0.5T and the loss P0.05 5 / 20K ≤ 25W / kg, so it has obvious advantages in high-power electronic transformer. In 50 kHz to 100 kHz electronic transformer, the loss of iron-based nanocrystalline alloy is P0.05 2 / 100k is 30 ~ 75W / kg, Fe based amorphous alloy P0.05 2 / 100k is 30W / kg, which can replace some ferrite markets.
As one of Transmart Industrial’s multiple product series, mumetal cores series enjoy a relatively high recognition in the market. Transmart Industrial provides diversified choices for customers. The mu-metal cores are available in a wide range of types and styles, in good quality and in reasonable price.Transmart Industrial effectively improves after-sales service by carrying out strict management. This ensures that every customer can enjoy the right to be served.
Hysteresis loss is the iron loss caused by the hysteresis phenomenon in the magnetization process of the iron core. The size of this loss is directly proportional to the area surrounded by the hysteresis loop of the material. The hysteresis loop of silicon steel is narrow, and the hysteresis loss of transformer core made of silicon steel is small, which can greatly reduce its heating degree. Since silicon steel has the above advantages, why not use the whole silicon steel as the iron core and process it into a sheet? rolled silicon steel sheet is selected. It is cut into long pieces according to the size of the required iron core, and then overlapped into “day” shape or “mouth” shape. In principle, in order to reduce eddy current, the thinner the silicon steel sheet, the narrower the spliced strip, and the better the effect. This not only reduces the eddy current loss and temperature rise, but also saves the material of silicon steel sheet. But in fact, when making silicon steel sheet iron core. Not only from the above favorable factors, because making the iron core in that way will greatly increase the working hours and reduce the effective section of the iron core. Therefore, when making transformer iron core with silicon steel sheet, we should start from the specific situation, weigh the advantages and disadvantages and choose the best size. Discover extra info at https://www.transmartcore.com/.
As the iron core of the transformer, generally 0.35mm thick cold-rolled silicon steel sheet is selected. It is cut into long pieces according to the size of the required iron core, and then overlapped into “day” shape or “mouth” shape. In principle, in order to reduce eddy current, the thinner the silicon steel sheet, the narrower the spliced strip, and the better the effect. This not only reduces the eddy current loss and temperature rise, but also saves the material of silicon steel sheet. But in fact, when making silicon steel sheet iron core. Not only from the above favorable factors, because making the iron core in that way will greatly increase the working hours and reduce the effective section of the iron core. Therefore, when making transformer iron core with silicon steel sheet, we should start from the specific situation, weigh the advantages and disadvantages and choose the best size.